KASON HTMV-1000A Auto Turret Micro-Vickers Hardness Tester
1 9 YEARS
Development Base of Advanced Testing Machine Of China
Instruction:
KASON HTMV-1000A Automatic Turret MicroHardness Tester is mainly used for the micro-Vickers hardness measurement of various metals and some non-metallic materials. ), non-ferrous metals, heat post-treated parts, various tiny and thin parts, glass, ceramics, agate, gemstones, etc. For hardness determination, and also suitable for carbonization, effective depth of quenching and hardening layer, coating, surface coating and welding
Heat-affected parts of parts. It can also be used to observe the internal metallographic structure of various metal parts and to collect and display images. It is especially suitable for measuring the hardness gradient distribution curve of the workpiece and measuring the surface hardness of the gear after heat treatment, and the depth of the effective hardened layer.
Technical Parameters:
|
Name |
Specification |
|
Test Force |
10gf、25gf、50gf、100gf、200gf、300gf、500gf、1kgf |
|
0.098N 、0.245N 、0.49N 、0.98N 、1.96N 、2.94N 、4.9N 、9.8N |
|
|
Convert Scales |
HRA 、HRB 、HRC 、HRD 、HRF 、HV 、HK 、HBW 、HR15N 、HR30N 、 HR45N、 |
|
Min. Unit of measurement |
0.025 μm |
|
Test Mode |
HV/HK |
|
Hardness Test Range |
5~3000HV |
|
Test Force Application Method |
Automatic (loading, dwelling, unloading) |
|
Turret Method |
Automatic |
|
Objective Lens |
10X 、40X |
|
Eyepiece |
10X |
|
Total Magnification |
100X (observation) 400X (measurement) |
|
Test Force Dwell Time |
1~60s |
|
X-Y Table Size |
100*100mm |
|
X-Y Test Table Maximum |
25*25mm |
|
Data Output |
LCD display readout |
|
Max. Height of Specimen |
110mm |
|
The Distance From the Center of |
110mm |
|
Power Supply |
AC220V±5％，50~60Hz |
|
Executive Standard |
ISO 6507 ，ASTM E384 ，JIS Z2244 ， GB/T 4340 .2 |
|
Dimensions |
405*290*480mm |
|
Net Weight |
40KG |